About Us | Careers | History | News | Extranet | Contact Us | Home
  Assembly Adhesives
Epoxy & Urethane Adhesives
& Potting

Aerospace Sealants & Adhesives Adhesives & Coatings for Inflatable Structures Contact & Pressure Sensitive Adhesives Water-based Adhesives
& Coatings
Energy Cured Adhesives
& Coatings
Flooring Adhesives & Accessories Mirror
Mastics
Custom Packaging  
 
Markets Served
 
Extranet Sign-In
Username
Password

Clifton Aircraft & Marine Inflatable Adhesives
Industrial Adhesives

Royal Adhesives & Sealants (Clifton division) manufactures a broad line of adhesives and coatings that meet Military Specification performance characteristics or are on the qualified product list.

LA 495 (MIL-C-2399B)

LA 495 has been qualified to MIL-C-2399A and is suitable for bonding cotton duck to cotton duck, vinyl to wood and vinyl to metal. The product may be applied by brush or roller as supplied.

  • Polymer Base: Nitrile rubber
  • Flash Point: < 0 deg. F. (TCC)
  • Color: Neutral
  • Weight/Gallon: 7.1 7.5

More


PC 903 (MIL-P9503-B)

PC 903 is a chlorosulfonated polyethylene based paint for factory and field applications involving fully erected rigid and air-supported radomes. It is an air-drying, synthetic elastomer-based paint meeting military specifications MIL-P9503-B. This coating, consisting of flammable solvents, dries to a tough non-tacky, flexible film, capable of handling 30 minutes after application under standard temperature and humidity conditions.

  • Polymer Base: Chlorosulfonated polyethylene
  • Flash Point: 40 deg. F (TCC)
  • Color: White or specified
  • Weight/Gallon: 8.5 +/- 0.5

More


FA 1005 (MMM-A-139)

FA 1005 is a two-part, self-curing, natural rubber adhesive used in the manufacture of inflatable lifeboats, life jackets, and equipment of similar nature. FA 1005 develops an exceptionally strong bond for natural rubber coated fabrics. It is recommended for use where excellent water resistance is required and where minimum creep at normal and elevated temperatures is desired. FA1005 is on the qualified products list for use with MMM-A-139B Types 1-3.

  • Polymer Base: Natural Rubber
  • Flash Point:
  • Color: Neutral
  • Weight/Gallon: 6

More


FA 1030 (Class 1-5) (MIL-A-5540B)

FA 1030 is a one or two-part, self-curing polychloroprene adhesive designed to bond coated fabrics and other materials. The excellent versatility of this adhesive makes it suitable for bonding synthetic rubber (Neoprene and Hypalon coated fabrics) and synthetic fabrics (nylon, dacron, rayon, etc.). FA 1030 conforms to MIL-A-5540B type 1 and 4 (heat cure) and type 2, 3, and 5 (room temperature cure) and MIL-C-7800 (paragraph 3,3,1.2) type 1 and 4 (heat cure) do not require accelerator.

  • Polymer Base: Polychloroprene
  • Flash Point: -21.7deg. F, -7 deg F (TCC)
  • Color: Neutral or Black
  • Weight/Gallon: 7.2 +/- .25 lbs

More


FA 1013 (Class 4 & 5) (MIL-A-5540B)

FA 1013 is a two-part, self-curing polychloroprene adhesive designed to bond coated fabrics and other materials. The excellent versatility of this adhesive makes it suitable for bonding synthetic rubber (Neoprene and Hypalon coated fabrics) and synthetic fabrics (nylon, dacron, rayon, etc.). FA 1013 conforms to MIL-A-5540B classes 4 & 5.

  • Polymer Base: Polychloroprene
  • Flash Point: -21.7 C, -7 deg. F (TCC)
  • Color: Neutral
  • Weight/Gallon: 7.18

More


FA 1065 (Class 3) (MIL-A-5540B)

FA 1065 is recommended for the manufacture and repair of Neoprene inflatables and meets MIL-A-5540 B, Classes 1 to 5. This product is also used in the repair of Hypalon coated fabrics.

  • Polymer Base: Polychloroprene
  • Flash Point: < 20 deg. F (TCC)
  • Color: Neutral
  • Weight/Gallon: 6.9

More


FA 1053 (Type I) (MMM-A-1617)

FA 1053 is recommended for bonding of cotton duck, leather, felt and cork to itself or to aluminum, steel and natural rubber. This adhesive meets Mil Spec. MMM-A-1617 Type I.

  • Polymer Base: Rubber
  • Flash Point: < 0 deg. F. (TCC)
  • Color: Neutral
  • Weight/Gallon: 6.55

More


FA 1051 (Type II) (MMM-A-1617)

FA 1051 is a one part adhesive, on the qualified products list for MMM-A-1617 Type 2.

  • Polymer Base: Polychloroprene
  • Flash Point: -7 deg. F (TCC)
  • Color: Neutral
  • Weight/Gallon: 7.08

More


FA 1076 (Type III) (MMM-A-1617)

FA 1076 is a solvent-based nitrile rubber adhesive formulated for bonding vinyl, nitrile-coated fabric, and cotton fabric sheeting to steel and aluminum. FA 1076 meets the requirements of Mil Spec. MMM-A-1617B, Type III.

  • Polymer Base: Nitrile
  • Flash Point: 14 deg. F (TCC)
  • Color: Neutral
  • Weight/Gallon: 7.2 +/- 0.2 #/gal

More


FA 1101 (MIL-S-43869A)

FA 1101 is a neoprene based, two-part room temperature curing adhesive formulated for the specific use of bonding cured neoprene, SBR, and hypalon coated fabrics to themselves or each other.

  • Polymer Base: Neoprene Rubber
  • Flash Point: 45 deg. F
  • Color: Neutral
  • Weight/Gallon: 7.3

More


E 1293 (MMM-A-121B)

E 1293 is designed for bonding vulcanized synthetic rubber gaskets, matting and similar items to steel. It will adhere to Neoprene, SBR, and Nitrile gasketing. E 1293 adhesive meets the requirements of Federal Specification MMM-A-121.

  • Polymer Base: Polychloroprene
  • Flash Point: < 0 deg. F. (TCC)
  • Color: Neutral
  • Weight/Gallon: 6.5 - 6.9

More


CC 5527 (A-A-1936)

CC 5527 is a fast drying brush and roller grade contact cement, which complies with Military Spec. A-A-1936 Type 1. It cures at room temperature, and is designed to bond decorative plastic to hard board, wood, metal, leather, fabrics, carpet backing and other materials.

  • Polymer Base: Polychloroprene rubber
  • Flash Point: -15 deg. F (TCC)
  • Color: Neutral
  • Weight/Gallon: 6.65 - 7.05

More


SS 3214 (MIL-P-43700B)

SS 3214 OR SS 3214M are polyurethane-based seam sealers for urethane-coated rucksacks ponchos.

SS 3214 and SS 3214M have excellent hydrostatic resistance and meet the specifications of MIL-L-43730A(GL), MIL-P-3003H, AND MIL-P-43700A.

  • Polymer Base: Polyurethane
  • Flash Point: 35 Deg. F
  • Color: Clear or light olive drab
  • Weight/Gallon: 7.2lbs

More


 
Additional Information
Product Categories
 
 
Industrial Adhesives
Product
Effect of Freezing
Storage Life
Solvent Clean Up
Solvent Dilution
Solids
Viscosity
Recommended Storage Conditions
More
CC 5527 (A-A-1936)
Reversible gel
12 mos
Toluene
Toluene
22 +/- 2%
300 - 700 cps, Brookfield RVT, #2, 20 RPM
45-85 Deg. F. Keep out of direct sunlight. Mix well before use.
more
E 1293 (MMM-A-121B)
Reversible gel
12 mos
Ketones & aromatic solvents
MEK/Toluene
18 +/- 1%
140 180 cps Brookfield RVT/ #1/ 20 RPM/ 78 F
45-85 Deg. F. Keep out of direct sunlight. Mix well before use.
more
FA 1005 (MMM-A-139)
Reversible gel
12 mos
Hexane or Toluene
Hexane
6.5 +/- 0.5%
2,000 3,000 cps Brookfield RVT/#4/ 20 RPM/ 78 F
45-85 Deg. F. Keep out of direct sunlight. Mix well before use.
more
FA 1013 (Class 4 & 5) (MIL-A-5540B)
Reversible gel
12 mos
Toluene
Toluene
26 +/- 2%
1000 - 1500 cps Brookfield RVT/#4/20 RPM/ 78 F
45-85 Deg. F. Keep out of direct sunlight. Mix well before use.
more
FA 1030 (Class 1-5) (MIL-A-5540B)
Reversible gel
12 mos
Toluene
Toluene
23 +/-2%
800 - 1300 cps Brookfield RVT/#3/20 RPM/ 78 F
45-85 Deg. F. Keep out of direct sunlight. Mix well before use.
more
FA 1051 (Type II) (MMM-A-1617)
Reversible gel
12 mos
Toluene
Toluene
25 +/- 2%
1100 1300 cps Brookfield RVT/#3/20 RPM/78 F
45-85 Deg. F. Keep out of direct sunlight. Mix well before use.
more
FA 1053 (Type I) (MMM-A-1617)
Reversible gel
12 mos
Toluene
Hexane
40 +/- 2%
1800 2200 cps Brookfield RVT/#3/20 RPM/78 F
45 - 85 Deg. F. Keep out of direct sunlight. Mix well before use.
more
FA 1065 (Class 3) (MIL-A-5540B)
Reversible gel
12 mos
Toluene
Toluene
25 % +/- 1%
1100 1300 cps Brookfield RVT/#3/20 RPM/78 F
45-85 Deg. F. Keep out of direct sunlight. Mix well before use.
more
FA 1076 (Type III) (MMM-A-1617)
Reversible gel
12 mos
MEK
MEK
26% +/- 1%
1,700 2,000 cps Brookfield RVT #4 Spindle,20 RPM, 78F
45-85 Deg. F. Keep out of direct sunlight. Mix well before use.
more
FA 1101 (MIL-S-43869A)
Reversible gel
12 mos
Toluene
Toluene
20%
1200-1500 cps
45-85 Deg. F. Keep out of direct sunlight. Mix well before use.
more
LA 495 (MIL-C-2399B)
Reversible gel
12 mos
Ketones
Acetone
30% miniumum
3,000 6000 cps Brookfield RVT/#4/20 RPM/78 F
45-85 Deg. F. Keep out of direct sunlight. Mix well before use
more
PC 903 (MIL-P9503-B)
Reversible gel
9 mos
TH 903
TH 903
23 +/- 2%
8 15 seconds (1/4 Ford Cup)
45-85 Deg. F. Keep out of direct sunlight. Mix well before use.
more
SS 3214 (MIL-P-43700B)
Reversible gel
12 mos
Mek Acetone
Mek Acetone
19%
1900-2400 cps
45-85 DEG. F Keep out of direct sunlight, and away from heat sources.
more
             

Under no circumstance will Royal Adhesives & Sealants LLC. or its subsidiaries, the manufacturer, or the seller of its products be liable for incidental or consequential damages arising from the use of any of its products. Any damages in connection with the use of any of Royal's products by the buyer, seller, user or any other person are strictly limited to the purchase price of the product only. Customer accepts full responsibility. All installation guidelines must be followed. Refer to literature or call 574-246-5000 for installation guidelines.

 

©Copyright 2005-2014 Royal Adhesives & Sealants. All Rights Reserved.